Title: High Thermoelectric Performance and Enhanced Mechanical Stability of p-type Ge1-xSbxTe
Authors: Perunnal, Suresh
Roychowdhury, Subhajit
Negi, Devendra S.
Datta, Ranjan
Biswas, Kanishka
Keywords: Physical Chemistry
Materials Science
Germanium Antimony Tellurides
Valence-Band Convergence
Bulk Thermoelectrics
GeTe
Alloys
PbTe
Figure
Merit
Nanostructures
Transport
Issue Date: 2015
Publisher: American Chemical Society
Citation: Chemistry of Materials
27
20
Perunnal, S.; Roychowdhury, S.; Negi, D. S.; Datta, R.; Biswas, K., High Thermoelectric Performance and Enhanced Mechanical Stability of p-type Ge1-xSbxTe. Chemistry of Materials 2015, 27 (20), 7171-7178.
Abstract: High thermoelectric figure of merit, zT, of similar to 1.85 at 725 K along with significant cydable temperature stability was achieved in Pb-free p-type Ge1-xSbxTe samples through simultaneous enhancement in Seebeck coefficient and reduction of thermal conductivity. Sb doping in GeTe decreases the carrier concentration due to the donor dopant nature of Sb and enhances the valence band degeneracy by increasing the cubic nature of the sample, which collectively boost Seebeck coefficient in the temperature range of 300-773 K. Significant thermal conductivity reduction was achieved due to collective phonon scattering from various mesa-structured domain variants, twin and inversion boundaries, nanostructured defect layers, and solid solution point defects. The high performance Ge0.9Sb0.1Te sample shows mechanical stability (Vickers microhardness) of similar to 206 Hv, which is significantly higher compared to other popular thermoelectric materials such as Bi2Te3, PbTe, PbSe, Cu2Se, and TAGS.
Description: Restricted access
URI: http://hdl.handle.net/10572/1986
ISSN: 0897-4756
Appears in Collections:Research Articles (Ranjan Datta)

Files in This Item:
File Description SizeFormat 
252.pdf
  Restricted Access
1.29 MBAdobe PDFView/Open Request a copy


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.